ABS	S100
Properties	Rated value	Test Method
Physical properties
Specific Gravity	1.04 g/cm3	ISO 1183/B
	1.05 g/cm3	ISO 1183/B
Apparent density	0.600 g/cm3	ISO 60
Die shrinkage, parallel	0.4 - 0.7 %	ASTM D955;ISO294-4
Melt index, mass
230 °C;3.8 kg	2.5 g/10min	ASTM D1238
10 kg;220 °C	10 g/10min	ISO 1133
Mechanical properties
Tensile strength, fracture	25.0 MPa	ASTM D638
Tensile strength, yield (5.1 mm/min)	42.3MPa	ASTM D638-1
Tensile strain, fracture (51 mm/min)	25%	ASTM D638-1
Tensile strain, yield (Thickness; 3.2mm)	3.30%	ISO 527-2/50
Tensile modulus
5 mm/min	2070 MPa	ASTM D638-1
Thickness; 3.2 mm	2200 MPa	ISO 527-2
Bending strength
5.1 mm/min	64.5 MPa	ASTM D790-1
Thickness; 3.2 mm	65.0 MPa	ISO 178
Bending modulus
	2210 MPa	ASTM D790
Thickness; 3.2 mm	2100 MPa	ISO 178
Impact strength of cantilever beam, notch
Thickness; 3.2 mm;Temperature; 23 °C	310 J/m	ASTM D256
Temperature; -30 °C	10.0 kJ/m2	ISO 108-1A
Temperature; 23 °C	17.0 kJ/m2	ISO 108-1A
Impact strength of simple supported beam, notch
Temperature; -30 °C	8 kJ/m2	ISO 179-2
Temperature; 23 °C	12 kJ/m2	ISO 179-2
Temperature; -30 °C	11 kJ/m2	ISO 179 1eA
Temperature; 23 °C	17 kJ/m2	ISO 179 1eA
Meter impact test, total energy
Thickness; 3.2 mm;Temperature; 23 °C;3.39 m/sec;Peak Energy	31.1 J	ASTM D3763
Thickness; 3.2 mm;Temperature; -29 °C;3.39 m/sec;Peak Energy	31.7 J	ASTM D3763
Thickness; 3.2 mm;Temperature; -29 °C;Total Energy	34.3J	ASTM D3763
Thickness; 3.2 mm;Temperature; 23 °C;-29 °C;Total Energy	45.4 J	ASTM D3763
Thermal properties
Linear coefficient of thermal expansion (CTE), parallel	94.0 μm/m-°C	ASTM D696
Heat Deflection Temperature
Thickness; 3.2 mm;Pressure; 0.46 MPa	96.1 °C	ASTM D648
Thickness; 3.2 mm;Pressure; 1.8 MPa	82.8 °C	ASTM D648
Pressure; 1.8 MPa;Annealed	101 °C	ISO 75-2/A
Vicat temperature	102 °C	ISO 306/B50
	108 °C	ASTM D1525
Flame retardant rating
Thickness; 1.5 mm	HB	UL 94
Thickness; 3 mm	HB	UL 94
Flame spread	60.0 mm/min	ISO 3795